Standards:
|
Q235 10 inch Carbon Steel Pipe |
GB |
ASTM |
DIN |
JIS |
ISO |
|
Q235A |
Gr.D |
|
SS440 SM400A |
E235B |
|
|
Q235B |
S235JR S235JRG1 S235JRG2 |
||||
|
Q235C |
Gr.D Gr.65 |
S235JO |
SM400A SM400B |
E235C |
|
|
Q235D |
Gr.D |
S235J2G3 S235J2G4 |
SM400A |
E235D |
Properties:
Chemical properties:
|
Q235 Pipe |
Grade |
C |
Si |
Mn |
P |
S |
|
A |
≤0.22 |
≤0.35 |
≤1.40 |
≤0.045 |
≤0.050 |
|
|
B |
≤0.20 |
≤0.045 |
||||
|
C |
≤0.17 |
≤0.040 |
≤0.040 |
|||
|
D |
≤0.035 |
≤0.035 |
Mechancal properties:
|
Q235 Steel Pipe |
Grade |
Yield Strength ReH/(N/mm2) |
Tensile strength Rm/(N/mm2) |
Elongation after break A/% |
||
|
Thickness (or diameter)/mm |
Thickness (or diameter)/mm |
|||||
|
A B C D |
≤16 |
≥235 |
370~500 |
≤40 |
≥26 |
|
|
＞16~40 |
≥225 |
＞40~60 |
≥25 |
|||
|
＞40~60 |
≥215 |
＞60~100 |
≥24 |
|||
|
＞60~100 |
≥215 |
＞100~150 |
≥22 |
|||
|
＞100~150 |
≥195 |
＞150~200 |
≥21 |
|||
|
＞150~200 |
≥185 |
|
|
|||
|
Q235 Carbon Steel Pipe |
Grade |
Impact test (V-notch) |
|
|
temperature/℃ |
Impact absorption energy (longitudinal)/J |
||
|
A |
- |
|
|
|
B |
+20 |
27 |
|
|
C |
0 |
||
|
D |
-20 |
||
| Q235 10 inch Carbon Steel Pipe | Specimen Direction | Cold bending test 180° B=2α | |
| Steel thickness (or diameter) / mm | |||
| ≤60 | ＞60~100 | ||
| Center diameter d | |||
| vertical | 0.5α | 1.5α | |
| horizontal | α | 2α | |
Characteristic:
Q235 10 inch carbon steel pipe, also known as A3 steel, is a common carbon structural steel.Q represents the yield limit of this carbon steel pipe, and the latter 235 refers to the yield value of this carbon steel pipe, which is about 235MPa.
But the yield value of Q235 pipe will decrease with the increase of thickness. Due to the moderate carbon content of Q235 steel pipe, good comprehensive performance, good matching of strength, plasticity and welding performance, Q235 steel pipe is the most widely used.
Industry&Application:
Q235 10 inch carbon steel pipes have the largest output and are widely used. They are mainly used in building structures such as factories, bridges, ships, and general pipelines for conveying fluids.Q235 carbon steel pipes are generally used directly without heat treatment.
Q235 10 inch carbon steel pipe can be used to transport low-pressure fluid, and Q235 steel pipe can also be used to manufacture various abrasive tool handles and other unimportant abrasive tool parts.Q235 pipe is used as the punch material, which can be used directly without tempering after quenching. The hardness is 36~40HRC, which solves the phenomenon that the punch is broken during use.
FAQ:
Q:Can you send samples?
A:Sample can be for free,freight cost collect.
Q:What product information do I need to provide?
A:Steel grade/thickness/width/quantity,these will decide the price.
Q:About product prices?
A:Prices vary from period to period due to cyclical changes in the price of raw materials.
Q:What are the certifications for your products?
A:We have ISO 9001,CE,SGS,BV and other certifications.
Q:How about the delivery time?
A:Regularly the delivery time around 10-15 days,customized one will inform the delivery time ahead.
Q:Does the product have quality inspection before loading?
A:All the products are strictly tested before packaging,also can inspect by third party inspection.
Q:How to pack the products?
A:Standard export package with waterproof film and wooden pallet.It can effectively protect products from corrosion.