410 410S Stainless Steel Coil-JIANGSU DINGJIN IRON & STEEL CO., LTD.

Purchasing Information

Product name	410 vs 410S Stainless Steel Coil
Technology	Cold Rolled; Hot Rolled
Thickness	0.2mm - 60mm
Width	3.2mm - 2000mm
Length	AS PER CUSTOMER'S REQUIREMENT
Type of Material	STAINLESS STEEL SOFT, DEEP DRAW, EXTRA DEEP DRAW, QUARTER HARD, HALF HARD,FULL HARD.
Finish	NO.1, 2B, 2D, 2H, 2R, No.4, HAIRLINE, SCOTCH BRITE, SATIN FINISH, NO.8, BA.
Standard	ASME, ASTM, AISI, EN, BS, GB, DIN, JIS, SUS, etc.
Certification	SGS, BV, IQI, TUV, ISO, CE, etc
Coil Weight	3-10 Tons Or As Your Requirements
Tolerance	±1%
MOQ	1 ton
Supply Ability	5000 tons / month
Lead Time	10-15 working days after the receipt of 30% deposit
Payment Terms	30%T/T Advance + 70% Balance
Price Terms	FOB, CFR, CIF, EXW
Packing	Standard sea-worthy package or as required
*If you do not find what you are looking for, please call us now. If you have found it, we are happy to answer any questions or concerns you may have about stainless steel grades and assist you through the purchasing process.

Characteristic

Standards:

Grade

ASTM

JIS

ISO

410S

06Cr13

0Cr13

S41008

410S

SUS410S

X6Cr13

1.4000

410

12Cr13

1Cr13

S41000

410

SUS410

X12Cr13

1.4006

Properties:

Chemical properties:

Grade	C	Si	Mn	P	S	Ni	Cr
410S	≤0.08	≤1.00	≤1.00	≤0.040	≤0.030	≤0.60	11.50~13.50
410	≤0.15	≤1.00	≤1.00	≤0.040	≤0.030	≤0.60	11.50~13.50

Mechancal properties:

Grade	Yield Strength R_P0.2/MPa	Tensile Strength R_m/MPa	Elongation after break A/%	180°bending test Bending head diameter D	Hardness value
Grade	Yield Strength R_P0.2/MPa	Tensile Strength R_m/MPa	Elongation after break A/%	180°bending test Bending head diameter D	HBW	HRB	HV
410S	≥205	≥415	≥22	D=2α	≤183	≤89	≤200
410	≥205	≥450	≥20	D=2α	≤217	≤96	≤210

Physical properties:

Grade	410S Stainless Steel Coil	410 Stainless Steel Coil
Density/（kg/dm³）20℃	7.75	7.70
Melting Range/℃	-	1480~1530
Specific Heat[kJ/(kg•K)]0℃~100℃	0.46	0.46
Thermal Conductivity/[W/(m•K)]	100℃: 25.0	100℃: 24.2
Thermal Conductivity/[W/(m•K)]	500℃: -	500℃: 28.9
Coefficient of Thermal Expansion/(10^-6/K)	0℃~100℃: 10.6	0℃~100℃: 11.0
Coefficient of Thermal Expansion/(10^-6/K)	0℃~500℃: 12.0	0℃~500℃: 11.7
Electrical Resistivity/(Ω•mm²/m)20℃	0.60	0.57
Modulus of Elasticity(kN/mm²)20℃	220	200
Magnetism	YES	YES

Application:

410 stainless steel coil:

410 Stainless Steel Coil is a general purpose martensitic stainless steel for highly stressed components containing 11.5%-13.50% chromium sufficient to demonstrate corrosion resistance in mild atmospheres, steam and many mild chemical environments. Therefore, 410 martensitic stainless steel coil has good corrosion resistance as well as high strength and hardness.

410 Stainless Steel Coil exhibits maximum corrosion resistance when hardened, tempered and polished, and is available in a hardened but still machinable condition for applications requiring high strength and moderate heat and corrosion resistance.Suitable for general knife blades, cutlery (spoon, fork, knife, etc.).

410S stainless steel coil:

410S Stainless Steel Coil is a low carbon non-hardening variant of 410 Stainless Steel Coil.

The 0.15% carbon content of 410S martensitic stainless steel minimizes the formation of austenite at high temperatures, which limits the steel's ability to harden. Even with rapid cooling from above the critical temperature, 410S coils remain soft and ductile.

This non-hardening characteristic helps prevent cracking when 410S martensitic stainless steel coils are exposed to high temperatures or welded. 410S stainless steel coils are completely ferritic in the annealed condition and exhibit similar corrosion resistance and good oxidation resistance as 410 stainless steel coils.

Stainless Steel Surface:

Surface Finish	Definition	Application
2B	Those finished, after cold rolling, by heat treatment, pickling or other equivalent treatment and lastly by cold rolling to given appropriate luster.	Medical equipment, Food industry, Construction material, Kitchen utensils.
BA	Those processed with bright heat treatment after cold rolling.	Kitchen utensils, Electric equipment, Building construction.
NO.3	Those finished by polishing with No.100 to No.120 abrasives specified in JIS R6001.	Kitchen utensils, Building construction.
NO.4	Those finished by polishing with No.150 to No.180 abrasives specified in JIS R6001.	Kitchen utensils, Building construction, Medical equipment.
HL	Those finished polishing so as to give continuous polishing streaks by using abrasive of suitable grain size.	Building Construction.
NO.1	The surface finished by heat treatment and pickling or processes corresponding there to after hot rolling.	Chemical tank, pipe.
Stainless steel has a variety of surfaces, please contact us for confirmation.

FAQ:

Q:Can you send samples?

A:Sample can be for free,freight cost collect.

Q:What product information do I need to provide?

A:Steel grade/thickness/width/quantity,these will decide the price.

Q:About product prices?

A:Prices vary from period to period due to cyclical changes in the price of raw materials.

Q:What are the certifications for your products?

A:We have ISO 9001,CE,SGS,BV and other certifications.

Q:How about the delivery time?

A:Regularly the delivery time around 10-15 days,customized one will inform the delivery time ahead.

Q:Does the product have quality inspection before loading?

A:All the products are strictly tested before packaging,also can inspect by third party inspection.

Q:How to pack the products?

A:Standard export package with waterproof film and wooden pallet.It can effectively protect products from corrosion.