Standards:
|
GB: |
022Cr19Ni10 |
|
00Cr19Ni10 |
|
|
ASTM: |
S30403 |
|
304L |
|
|
JIS: |
SUS304L |
|
ISO: |
X2CrNi18-9 |
|
EN: |
X2CrNi18-9 |
|
1.4307 |
Properties
Chemical properties:
|
304L Stainless Steel Sheet |
C |
Si |
Mn |
P |
S |
Ni |
Cr |
N |
|
≤0.030 |
≤0.75 |
≤2.00 |
≤0.045 |
≤0.030 |
8.00~12.00 |
17.50~19.50 |
≤0.10 |
Mechancal properties:
|
304L Stainless Steel |
Yield Strength |
Tensile Strength |
Elongation after break |
Hardness value |
||
|
HBW |
HRB |
HV |
||||
|
≥180 |
≥485 |
≥40 |
≤201 |
≤92 |
≤210 |
|
Physical properties:
|
304L Stainless Steel Plate |
|
|
Density/（kg/dm³）20℃: |
7.90 |
|
Melting Range/℃: |
- |
|
Specific Heat[kJ/(kg•K)]0℃~100℃: |
0.50 |
|
Thermal Conductivity/[W/(m•K)]: |
100℃: 16.3 |
|
500℃: 21.5 |
|
|
Coefficient of Thermal Expansion/(10-6/K): |
0℃~100℃: 16.8 |
|
0℃~500℃: 18.3 |
|
|
Electrical Resistivity/(Ω•mm2/m)20℃: |
- |
|
Modulus of Elasticity(kN/mm2)20℃: |
- |
Characteristic:
304L stainless steel sheet is a 300 series austenitic stainless steel with carbon content reduced to 0.030% on the basis of 304 stainless steel plate, so it shows a lower corrosion rate than 304 stainless steel plate. But in most corrosive environments, the corrosion resistance of 304L steel is the same as that of 304 steel.
304L stainless steel has superior intergranular corrosion resistance and excellent welding performance. It does not require post-weld annealing. Therefore, it is preferred to be used in environments where intergranular corrosion is prone to occur in welds and heat-affected zones of sensitive alloys. If you care about welding quality, it is recommended to choose 304L stainless steel instead of 304 steel.
304L stainless steel plate has better heat resistance and is more resistant to carbide precipitation. It can be heated to a temperature range of 1148 ° C to 1260 ° C during forging.
The processing performance of 304L steel is no different from that of 304 steel, and both can be stretched and formed. However, in order to eliminate the stress generated during processing, it should be annealed or stress relieved as soon as possible after processing.
Application:
The industry and application of 304L stainless steel plate are the same as 304 steel, but it is recommended to choose 304L steel when the welding quality is the main factor.
FAQ:
Q:Can you send samples?
A:Sample can be for free,freight cost collect.
Q:What product information do I need to provide?
A:Steel grade/thickness/width/quantity,these will decide the price.
Q:About product prices?
A:Prices vary from period to period due to cyclical changes in the price of raw materials.
Q:What are the certifications for your products?
A:We have ISO 9001,CE,SGS,BV and other certifications.
Q:How about the delivery time?
A:Regularly the delivery time around 10-15 days,customized one will inform the delivery time ahead.
Q:Does the product have quality inspection before loading?
A:All the products are strictly tested before packaging,also can inspect by third party inspection.
Q:How to pack the products?
A:Standard export package with waterproof film and wooden pallet.It can effectively protect products from corrosion.